- Seals dentinal tubules and minimizes post-operative sensitivity
- Low film thickness
- High Compressive strength
- Radiopaque
- Neutralizes the hardness of phosphoric acid
- Apply directly to prepared dentinal tissue
- Prevest DenPro (30014) Zinc F +
Zinc F+ is a zinc phosphate cement suitable for the cementation of crowns, bridges, inlays facings, and orthodontic brackets. May also be used for cavity lining under all restorative materials, temporary fillings, and fillings in deciduous teeth.
Zinc F+ is a zinc phosphate cement that has universal application for crowns and bridges and as a liner/core or base material. Zinc F+ offers an extremely accurate fit with very high mechanical strength.
BENEFITS:
High-strength bases offering good pulpal protection
Modulus of elasticity close to tooth structure
Excellent luting cement with high retentive rates
INDICATIONS :
Cavity lining under all restorative materials.
Cementation of crowns & bridges, inlays, and orthodontics brackets.
Temporary restoration
Restoration in deciduous teeth
TECHNICAL DATA:
Mixing time: 60-90 seconds
Setting time: 3:15 sec (luting): 3:10 sec (Base)
Film thickness: 22um
Compressive strength: 105 Mpa
COMPOSITION:
Powder : Zinc Oxide, Magnesium Oxide, and Sodium Fluoride.
Liquid: Aqueous solution of Phosphoric acid.
Contraindications: Direct or indirect pulp-capping.
Storage Conditions: Store at a temperature between 10°C to 24°C. Close the cap carefully after use. Keep Away from Moisture. Shelf life is not affected after opening if stored in a cool dry place.
- Seals dentinal tubules and minimizes post-operative sensitivity
- Low film thickness
- High Compressive strength
- Radiopaque
- Neutralizes the hardness of phosphoric acid
- Apply directly to prepared dentinal tissue
- Prevest DenPro (30014) Zinc F +
Zinc F+ is a zinc phosphate cement suitable for the cementation of crowns, bridges, inlays facings, and orthodontic brackets. May also be used for cavity lining under all restorative materials, temporary fillings, and fillings in deciduous teeth.
Zinc F+ is a zinc phosphate cement that has universal application for crowns and bridges and as a liner/core or base material. Zinc F+ offers an extremely accurate fit with very high mechanical strength.
BENEFITS:
High-strength bases offering good pulpal protection
Modulus of elasticity close to tooth structure
Excellent luting cement with high retentive rates
INDICATIONS :
Cavity lining under all restorative materials.
Cementation of crowns & bridges, inlays, and orthodontics brackets.
Temporary restoration
Restoration in deciduous teeth
TECHNICAL DATA:
Mixing time: 60-90 seconds
Setting time: 3:15 sec (luting): 3:10 sec (Base)
Film thickness: 22um
Compressive strength: 105 Mpa
COMPOSITION:
Powder : Zinc Oxide, Magnesium Oxide, and Sodium Fluoride.
Liquid: Aqueous solution of Phosphoric acid.
Contraindications: Direct or indirect pulp-capping.
Storage Conditions: Store at a temperature between 10°C to 24°C. Close the cap carefully after use. Keep Away from Moisture. Shelf life is not affected after opening if stored in a cool dry place.